"Particle sliding in ceramic LaMnO3"
H.R. Salva, A.A. Ghilarducci, A.G. Leyva and S.S. Seiro
Proc. of the "17th International Conference on Magnetism" (ICM 2006), Kyoto, Japan, August 20-25, 2006. Ed. H. Harima, H. Kawamura, Y. Kitaoka, H. Kohno, K. Miyake, Y. Suzuki, H. Sakakima and G.-q. Zheng
J. Magn. Magn. Mater. 310(2), Part 2 (2007) c626-c628
We measured the anelastic spectra of LaMnO3. An internal friction peak appears at 300-350 K depending on the sample preparation. Two methods of preparation of the sample were used changing also the sintering time and temperature The IF peak disappears when the sample was sintered for 79 h at 1400 C. The grains show soldered. When the grains are not soldered an IF peak is obtained with its corresponding modulus drop. Applying the theory of grain-boundary sliding, proposed by C. Zener in 1941, the Poisson ratio χ=0.38(5) and 0.43(5) could be obtained.
Av. Gral Paz y Constituyentes, San Martín, Pcia. de Buenos Aires, Argentina
Tel: (54-11) 6772-7007 - Fax: (54-11) 6772-7121